Ultra-miniature electrical contacts and method of manufacture

ABSTRACT

Ultra-miniature electrical contacts are provided with the strength and resilience necessary to give stable low resistance connection, to minute areas of a device, such as a thousand or so closely spaced surface pads of an integrated circuit. Each contact is initially formed on a substrate as a thin, narrow elongated flat body comprised of selectively deposited layers of metal. Depending on the final configuration desired for the contact, the metal of one metal layer has a coefficient of thermal expansion such as chromium (Cr), and the metal of another layer has a coefficient of thermal expansion such as copper (Cu). Each contact is permanently formed (by differential expansion of the metal layers when heated) into a three-dimensional structure and is then made “robust” by a covering of a specialized stiffening metal plating which adds substantial strength to the contact. This also makes the contact “springy” and enables the contact to be deformed substantially without permanent deformation or “set”. Such ultra-miniature contacts are made using photolithography and techniques for deposition of metals and other materials onto a substrate, as commonly used in the semiconductor industry.

CROSS-REFERENCE TO RELATED PATENT APPLICATION

This application is related to U.S. patent application Ser. No.08/942,623, filed Oct. 2, 1997, with inventors Robert B. Marcus andYanwei Zhang, and entitled “Micromachined Element And Method OfFabrication Thereof”. This above identified application is incorporatedherein by reference.

FIELD OF THE INVENTION

This invention relates to ultra-miniature electrical contacts which aresmall enough and robust enough to make contact directly and reliably tomicron size areas at any of numerous contact points on the face of anintegrated circuit (IC), for example.

BACKGROUND OF THE INVENTION

As integrated circuits (ICs) become denser and denser with thousands andeven millions of devices (e.g., memory cells, gates, etc.) on a singlechip, the problem of making connections between external circuits andthe devices on the chip becomes increasingly difficult. Frequently, achip is encapsulated in a package with contacts on the chip permanentlyconnected (e.g., by wire bonding, or otherwise), to relatively largeexternal contacts on the package, such as the pins on a dual in-linepackage (DIP). Especially where the devices on an IC operate at speedsin the gigahertz (GH_(z)) range, this method of connecting the internaldevices on the chip to external circuits can cause impedance mismatchingand imposes undesirable restraints on the overall speed of operation aswell as significant added costs. It would therefore be highly desirableto be able to make connections directly to the devices on the chip withminimal physical separation from other devices, or from one chip toanother.

Another widely used way to make connections to an IC is by means ofsolder “bumps” positioned in a pattern either on a substrate thatmatches the locations of the solder bumps to respective locations ofsmall surface pads on the IC, or on the IC itself. The solder bumps arepressed against the pads and then reflowed thereby making permanentinterconnections all at once. However, one disadvantage with this way ofinterconnection is that it results in a very rigid composite structure.The IC and substrate are held closely together with perhaps a thousandsoldered joints. Unless the coefficients of thermal expansion of the ICand of the substrate are closely matched, differential expansion of themembers when temperature changes during operation can cause rupture ofan interconnection or fracture of the IC or substrate. It is highlydesirable therefore that interconnections between an IC and a substratebe at least somewhat mechanically compliant. The present inventionprovides interconnections which while stable and low in resistance arealso compliant.

From a cost standpoint, it would also be highly desirable in order tomeet any particular or specific application to be able to assemble intoan overall circuit individual off-the-shelf chips before they are sealedinto separate packages. In order to do this to do this it must bepossible to test the operation of the circuit and its individual chipsbefore final packaging. Testing should be under conditions as nearly aspossible equal to actual operating conditions. This also means as apractical matter that one or more individual ICs in the overall circuit,in the event the circuit does not operate properly for a particularapplication, should be easily replaceable even though the individual IChas met general specifications for itself alone.

In the past there have been various attempts to provide electricalcontacts which meet the needs outlined above. Most if not all suchattempts have been not entirely successful because of one or moreshortcomings such as: not sufficiently small in size; or withoutadequate robustness to make stable electrical connections directly tocontact pads on the face of an IC, or without adequate compliance torepeatedly make contact to surface pads without permanent deformation or“set”, or without ease of manufacturing and of assembly with thenecessary high degrees of mechanical precision and electricalperformance.

As is well known in the art of electrical connections, a primerequirement for an electrical contact is that it be able to make astable and low resistance connection. To do this a contact should itselfhave high conductivity and enough physical strength (i.e., be robustenough) to exert adequate force against the member it is contacting. Acontact should also act against the member to break through or scrapeaway any oxide (or high resistance film) on the surface between contactand member. These requirements for stability and low resistance areextremely difficult to meet when it is also necessary that the size ofcontacts be minute enough to make simultaneous electrical connections toa thousand or so micron-size contact pads (e.g., 80 or so micronssquare) on an IC.

The present invention provides ultra-miniature electrical contacts whichare strong yet compliant, together with an efficient method ofmanufacturing and of precision assembly into electrical connectors,especially suitable for stable, low resistance temporary and/orpermanent connections to the closely spaced area array and/or edge arraycontact pods of very dense ICs. The present invention is an importantimprovement upon that described in U.S. patent application, Ser. No.08/942,623, filed Oct. 2, 1997, in the names of Robert B. Marcus andYanwei Zhang. The disclosure in said patent application is referred toherein and is explicitly incorporated by reference into the presentapplication.

SUMMARY OF THE INVENTION

In accordance with one aspect of the invention there are providedultra-miniature electrical contacts having improved performance andversatility. The design of one such contact insures that when it ispressed down against a surface pad on an IC for example, the contactwipes against the pad and breaks through or scrapes away oxide or otherhigh resistance film on the face of the pad. The contact is ofhigh-conductivity material and has ample strength and resilience to bearagainst the pad with enough force to insure stable, low resistanceelectrical contact Each contact is initially formed on a substrate as athin, narrow elongated flat body comprised of selectively depositedlayers of metal. Depending on the final configuration desired for thecontact, as illustrated hereinafter, the metal of a first metal layerhas a first coefficient of thermal expansion (α1), and the metal ofanother layer has a second thermal coefficient (α2), which is differentfrom α1. Each contact is formed into a three-dimensional structure (aswill be explained hereinafter) and is then made strong by a covering ofa specialized metal plating which adds substantial stiffness andstrength to the contact. This also makes the contact “springy”(compliant) and enables the contact to be deformed substantially withoutpermanent deformation or “set”, a characteristic highly important tomultiple electrical contacts making connections to a large number ofsurface pads on a chip or to the surface pads on many chips in a planararray. This is especially so when making repeated connections to one ICafter another, as with a probe card for example.

Electrical contacts according to the invention are advantageouslyfabricated en masse on closely spaced and precisely located centers byphotolithography, and selective deposition of metals and other materialsthrough a series of process steps akin to ones employed in semiconductormanufacturing and which are well known. By way of example,ultra-miniature electrical contacts in accordance with the presentinvention are produced by: (a) providing a substrate, such as a siliconwafer, and depositing a thin insulating layer thereon, such as siliconnitride (Si₃N₄); (b) depositing a thin sacrificial layer, such as SiO₂;(c) patterning the sacrificial layer using photolithography, so thatstrips of the sacrificial layer left after patterning define, at leastroughly, the outline in planar form of each such electrical contact; (d)defining photographically the regions for metal deposition with photoresist thicker than the thickness of the metal to be deposited; (e)depositing (e.g., by sputtering) a layer of metal having a firstcoefficient of thermal expansion; (f) removing the resist along withunwanted metal; (g) depositing and patterning photoresist for a secondlayer of metal; (h) selectively depositing (e.g., by sputtering) a layerof metal having a thermal coefficient of expansion different from thefirst; (i) removing the resist along with unwanted portions of metal;(j) removing the sacrificial layer (e.g., using hydroflouric acid); (k)heating the planar contacts to “curl” or form them intothree-dimensional shapes of desired configuration; and (l) substantiallystrengthening the contacts by electroplating over them specializedstiffening metal. In addition special contact areas may be applied toeach electrical contact to provide a surface-scraping action whenpressed against another contact member, such as a surface pad on anintegrated circuit (IC).

In accordance with another apparatus aspect, the present invention isdirected to an ultra-miniature electrical contact which has an elongatedconductive body formed of at least two layers of different metalsselectively deposited upon each other, a portion of the contact beingadapted to be fixed to a substrate, another portion of the contact beingpermanently bent above the substrate as a result of differentialexpansion of metal layers, and an outer stiffening metal layer beingdeposited over the plurality of metal layers, such that the contact hassufficient strength and resilience to effect stable low-resistanceconnection to another contact member.

Viewed from another apparatus aspect, the present invention is directedto an ultra-miniature electrical contact comprising an elongatedconductive body having two ends and formed of at least three layers ofmetals selectively deposited upon each other. The layers comprise aninner layer, a middle layer, and an outer layer with the middle layerbeing located between at least one portion of each of the inner andouter layers, the middle metal layer having a coefficient of thermalexpansion that is different from that of other layers. One end of thebody of the contact is adapted to be affixed to a substrate. The body ofthe contact is bent above the one end of the contact and the substrate.At least a portion of the body of the contact near its other end is bentdown toward the substrate by differential expansion of metal layers.

Viewed from another apparatus aspect, the present invention is directedto an ultra-miniature electrical contact comprising an elongatedconductive body formed of a plurality of two or more layers of differentmetals selectively deposited upon each other and an outer stiffeningmetal layer. A portion of the contact is adapted to be fixed to asubstrate. Another portion of the contact is permanently bent above thesubstrate as a result of differential expansion of metal layers. Anouter stiffening metal layer is deposited over the plurality of metallayers such that the contact has sufficient strength and resilience toeffect stable low-resistance connection to another contact member.

Viewed from another apparatus aspect, the present invention is directedto an assembly of ultra-miniature electrical contacts mounted on asubstrate and suitable for contacting contact areas of a device such asan integrated circuit. At least one of the ultra-miniature electricalcontacts comprises an elongated conductive body having two ends andformed of at least three layers of metals selectively deposited uponeach other. One inner metal layer has a coefficient of thermal expansionthat is different from that of other layers. One end of the body of thecontact is adapted to be affixed to the substrate, the body of thecontact by differential expansion of metal layers being bent above theone fixed end of the contact and the substrate. At least a portion ofthe body of the contact near its other end is bent down toward thesubstrate as a result of differential expansion of metal layers. Anouter stiffening metal layer is electrodeposited on the other layers togive substantial strength and resiliency to the contact.

Viewed from another apparatus aspect, the present invention is directedto an assembly of ultra-miniature electrical contacts mounted on asubstrate and suitable for contacting surface pads of a device such asan integrated circuit (IC). The assembly comprises a substrate with anelongated conductive body formed on the substrate as a plurality oflayers of different metals selectively deposited upon each other. Aportion of the contact is affixed to the substrate. A remaining portionof the contact is permanently bent into a three-dimensional shape abovethe substrate as a result of differential expansion of metal layers. Anouter stiffening metal layer is deposited over the plurality of metallayers such that the contact has sufficient strength and resilience toeffect stable low-resistance connection to a surface pad of an ICdevice.

Viewed from a method aspect, the present invention is directed to amethod of forming ultra-miniature electrical contacts. The methodcomprises the steps of: defining by photolithography an elongated areaor areas on a substrate; selectively depositing within each area aninner layer, a middle layer, and an outer layer of metals deposited uponeach other to form a conductive body of the contact with the middlemetal layer having a coefficient of thermal expansion higher than thatof other layers and one end of the contact being fixed to the substrate;and heating the body of the contact so that by differential expansion ofthe metal layers the contact for most of its length beyond its fixed endis bent above the substrate, and at least a portion of the body near itsother end is bent down toward the substrate.

Viewed from another method aspect, the present invention is directed toa method of forming ultra-miniature electrical contacts. The methodcomprises the steps of: defining by photolithography an elongated areaor areas on a substrate; selectively depositing within each area aplurality of layers of metal upon each other to form a conductive bodyof a contact with one metal layer having a coefficient of thermalexpansion higher than that of another layer and one end of the contactbeing fixed to the substrate; heating the body of the contact so that bydifferential expansion of metal layers the contact for most of itslength beyond its fixed end is bent above the substrate, and at least aportion of the body near its other end is bent down toward thesubstrate; and over-plating with an outer stiffening metal layer theother metal layers to give substantial strength and resiliency to thecontact.

In accordance with yet another method aspect, the present invention isdirected to a method of forming an assembly of ultra-miniatureelectrical contacts mounted on a substrate and suitable for contactingcontact areas of a device such as surface pads of an integrated circuit(IC). The method comprises the steps of: providing an insulatedsubstrate on which a pattern of conductive circuit traces can bedeposited; defining by photolithography elongated areas on the substratewhere contacts are to be located; depositing in each of the definedareas an elongated conductive body of a contact having a plurality oflayers of different metals selectively plated upon each other, an endportion of one metal layer being connected to a portion of conductivetraces on the substrate; heating each contact body so that bydifferential expansion of the metal layers the contact is permanentlybent into a three-dimensional shape above the substrate; and depositingan outer stiffening metal layer over the plurality of metal layers sothat the contacts have sufficient strength and resilience to effectstable lowresistance resistance connection to contact areas of a devicesuch as surface pads of an IC.

A better understanding of the invention together with a fullerappreciation of its many advantages will best be gained from a study ofthe following description given in connection with the accompanyingdrawing and claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic plan (top) view showing in exploded relation anelectrical circuit assembly of individual circuit chips in a planararray which are interconnected by means of ultra-miniaturesurface-contacting electrical contacts mounted on a substrate andprovided in accordance with the present invention;

FIG. 2 is a greatly enlarged schematic side view of an isultra-miniature card-edge electrical contact (clip) also provided by theinvention and showing it making contact to a surface pad on the edge ofa circuit chip;

FIG. 3 is a schematic side view of the ultra-miniature card-edgeelectrical contact of FIG. 2 at one stage of its fabrication inaccordance with a method of the present invention;

FIG. 4 is a view similar to FIG. 3 but at a later stage of fabricationof the contact;

FIG. 5 is a view of the electrical contact of FIG. 4 after the contacthas been formed into a three-dimensional shape;

FIG. 6 is a view of a partially fabricated electrical contact closelysimilar to the contact shown in FIG. 5;

FIG. 7 is a view of the electrical contact of FIG. 5 after it has beenover-plated with a stiffening metal for strength and resistance topermanent deformation;

FIG. 8 is a greatly enlarged side view of an ultra-miniaturesurface-contacting electrical contact (such as illustrated in FIG. 1) atone stage of its fabrication in accordance with a method of the presentinvention;

FIG. 9 is a view similar to FIG. 8 but at a later stage of fabricationof the contact;

FIG. 10 is a view of the electrical contact of FIG. 9 after it has beenformed into a three-dimensional shape and over-plated with a stiffeningmetal for strength and resistance to permanent deformation;

FIG. 11 is a schematic side view of the electrical contact shown in FIG.10 making initial contact with a surface pad of a circuit chip;

FIG. 12 is a schematic side view of the electrical contact of FIG. 11after scraping against the surface pad and being pressed into stable,low resistance contact with the pad.

FIG. 13 is an enlarged schematic side view partially broken away ofanother partially fabricated ultra-miniature surface-contactingelectrical connector also embodying features of the invention;

FIG. 14 is a plan (top) view of the connector shown in FIG. 13;

FIG. 15 is a schematic side view of a fully fabricated connector ofFIGS. 13 and 14 as it is about to engage a surface pad of a circuitchip; and

FIG. 16 is a similar view showing the connector of FIG. 15 after it hasengaged the surface pad of the chip.

The drawings are not necessarily to scale.

DETAILED DESCRIPTION

Referring now to FIG. 1, there is shown in schematic form a plan (top)view of an electrical circuit assembly 10 of a variety of chips 12 thatmay contain integrated circuits (ICs) microlectronic and/or sensordevices, etc. (designated C1 through C6) and mounted as a planar arrayon a support card 13. The chips 12 which have surface pads 15 facing“up” are electrically interconnected by a mating substrate 14 (shown inexploded relation to the chips 12 and the support card 13) having anarray of ultra-miniature surface-contacting electrical contacts,generally indicated at 16, and provided in accordance with the presentinvention. The ultra-miniature contacts 16 at their lower ends aremounted on the substrate 14 and interconnected in a desired pattern byconductive circuit traces (not shown). One or more of the chips 12 canbe removed from the support card 13 during testing and before finalencapsulation of the assembly 10 of chips 12 and contacts 16 can betested under actual, or nearly actual operating conditions, and one ormore chips 12 can easily be removed and replaced to achieve optimumperformance of the overall circuit. This is an important advantageprovided by the present invention. It is to be understood that when theplanar array of chips 12 on the surface card 13 is mated (as illustratedby an arrow 17) with the substrate 14 and its array of contacts 16 eachcontact 16 makes stable electrical connection to a respective surfacepad 15 on the faces of the chips 12. This will be explained in greaterdetail hereinafter.

Referring now to FIG. 2, there is shown, greatly enlarged, a schematicside view of an ultra-miniature card-edge electrical contact 20, and aportion of a board 22 on which one or more such contacts are mounted. Aswas mentioned previously in connection with the contacts 16, the lowerends of the contacts 20 are interconnected in a desired pattern byconductive circuit traces (not shown) on the board 22. Each contact 20makes connection to a respective one of surface pads 21 spaced along anedge of a chip 23, for example.

As was explained previously ultra-miniature electrical contacts inaccordance with the present invention are advantageously produced by thefollowing process steps: (a) providing a substrate, such as a siliconwafer; (b) depositing an insulating layer thereon, such as siliconnitride (Si₃N₄); (c) depositing a sacrificial layer, such as SiO₂; (d)patterning the sacrificial layer using photolithography, so that stripsof the layer left after patterning define, at least roughly, the outlinein planar form of each such electrical contact; (e) definingphotographically the regions for metal deposition with plating resistthicker than the thickness of the layers of metal to be used; (f)selectively depositing a layer of metal having a first coefficient ofthermal expansion α1; g) depositing a layer of metal having a secondcoefficient of thermal expansion α2 different from the first coefficientα1; (h) removing the resist along with unwanted portions of metal; (i)removing the sacrificial layer; (j) briefly heating the planar contactsto raise them partially above their substrate and form them intothree-dimensional shapes of desired configuration; and (k) substantiallystrengthening the contacts by electroplating over them specializedstiffening metal. Specific details of the process steps outlined aboveare well known to those skilled in the art and are not further describedherein. It is to be understood that the substrate 14 (or the board 22),during fabrication of the electrical contacts 16 (or the contacts 20),can have patterned on it interconnecting conductive circuit traces (notshown) to which respective ends of the contacts 16 (or the contacts 20)are connected during fabrication of the contacts. Techniques for formingsuch circuit traces are well known. It is also to be understood that forgood adhesion to the contacts to the insulating layer (where exposed bythe sacrificial layer) a very thin layer (e.g., a few nanometers thick)of a metal such as chromium or titanium may be deposited. The adhesionlayer is so thin compared to the metal layers forming the body of eachcontact that other physical properties of the adhesion layer such ascoefficient of thermal expansion are relatively unimportant.

Referring now to FIG. 3, there is shown an enlarged schematic side view,not to scale, of a partially fabricated ultra-miniature card-edgeelectrical contact 20 still in planar form. The structure shown herecomprises the board 22 (partially broken away); a layer of insulation 24(e.g., Si₃N₄); a thin sacrificial layer 26 (e.g., SiO₂); a short,selectively deposited (e.g., by sputtering) layer 28 of metal (e.g., Cr)with a relatively low coefficient of thermal expansion; a secondextensive layer 30 of metal (e.g., Cu) with a higher coefficient ofthermal expansion than that of the layer 28; and a third selectivelydeposited layer 32 of metal (e.g., Cr) in two portions 32 a and 32 bwith a thermal coefficient of expansion like to that of the layer 28.The extensive metal layer 30 forms the main body of the contact 20 andis joined at a fixed end 34 onto a portion of a conductive circuit trace(not shown) and the insulating layer 24. The contact 20 is therebyprecisely located and interconnected in a desired pattern with othercircuit elements (not shown) and the insulating layer 24. Other detailsin the fabrication of the contact 20, such as a very thin metal adhesionlayer, are not shown herein.

Referring to FIG. 4, the ultra-miniature card-edge contact 20, still inplanar form is shown after the sacrificial layer 26 has been removed(e.g., by hydroflouric acid) as here indicated by a dashed line. Thisfrees the body of the contact 20 along its length, except for the fixedend 34, so that it subsequently is able to move away from the test board22.

Referring to FIG. 5, the ultra-miniature card-edge contact 20 has beenformed into the three-dimensional shape shown by briefly heating (e.g.,at a suitable temperature above 300° C.). The differential expansionduring heating of the metal layer 30 (e.g., Cu) relative to the metallayers 32 a, 32 b, (e.g., Cr) plated on top of the layer 30 causes thepermanent upward bends indicated at 36 in the contact 20. Similarly thedifferential expansion during heating of the metal layer 30 relative tothe metal layer 28 (e.g., Cr) plated underneath the layer 30 causes apermanent downward bend indicated at 38. By controlling the respectivelengths and placement of the layers 28 and 32 a, 32 b and theirthicknesses relative to that of the layer 30, the card-edge contact 20can be given various desired shapes.

Referring now to FIG. 6, there is shown a partially fabricatedultra-miniature card-edge contact 20A, which is closely similar to thecontact 20 (FIG. 5) after it has been formed into a three-dimensionalshape by briefly heating (e.g., at a suitable temperature above 300°C.). Here, the contact 20A has a first or inner metal layer 29 formed intwo short-length portions 29 a and 29 b, a second or middle full lengthmetal layer 31, and a third or outer short length metal layer 33. Thelayers 29 a, 29 b, 31 and 33 are selectively deposited upon each otherin a series of steps closely similar to those illustrated in FIGS. 3 and4 for the contact 20. As seen in FIG. 6, the metal layer parts 29 a and29 b (e.g., Cu) have a higher coefficient of thermal expansion than thatof the middle metal layer 31 (e.g., Cr), and the outer metal layer 33(e.g., Cu) has a higher coefficient of thermal expansion than that ofthe middle layer 31. As a result the contact 20A has the same upwardbends 36 and the same downward bend 38 as does the contact 20 (FIG. 5).The contact 20A is anchored at its end 35 to the substrate 22 and theinsulating layer 24. The lengths and thicknesses of the metal layers 29a, 29 b, 31 and 33 are chosen to give the desired final shape to thecontact 20A. The length of the metal layer 31 can be similar to that ofthe metal layer 30 of the contact 20.

Referring now to FIG. 7, the ultra-miniature card-edge contact 20 in itsthree-dimensional form has now been over-plated with a stiffening metallayer 40. This greatly strengthens the contact 20 and enables it to besubstantially deformed without taking a permanent set. This is animportant feature of the present invention. By way of example, the metallayer 30 can have a length of about 600 to 800 microns, a width of about50 to 100 microns, and a thickness of a few microns. The lengths andthicknesses of the layers 28 and 32 a, 32 b are chosen to give thedesired final shape to the contact 20. The thickness of the metalstiffening layer 40 is a few microns. The layer 40 is advantageouslyformed by electroplating from a proprietary “Palladium M Series PlatingSolution” sold by Lucent Technologies. A metal layer (e.g., layer 40)formed from this solution has a Knoop hardness of about 600, which isvery much harder than precious metals normally used for electricalcontact areas (e.g., Knoop hardness of about 160 or less). It is to beunderstood that the contact 20A (FIG. 6) is also over-plated with anouter stiffening metal layer 40 and is interconnected to other suchcontacts in the same way as the contact 20.

Referring now to FIG. 8, there is shown an enlarged schematic side view,not to scale, of a partially fabricated ultra-miniaturesurface-contacting electrical contact 16 (see FIG. 1) still in planarform. The structure shown here comprises the substrate 14 (partiallybroken away), a layer 44 of insulation (e.g., Si₃N₄)), a thinsacrificial layer 46 (e.g., SiO₂), a selectively deposited (e.g., bysputtering) layer 50 of metal (e.g., Cr) with a relatively lowcoefficient of thermal expansion, a short layer 52 of a hard metal(e.g., W) and a layer 54 of insulation which masks the metal areasexcept where the layer 52 of hard metal is selectively deposited (e.g.,by sputtering).

Referring to FIG. 9, there is shown the ultra-miniaturesurface-contacting electrical contact 16 at a further stage offabrication. Here the insulating layer 54 (seen in FIG. 8) has beenstripped away (e.g., using hydroflouric acid), and a second layer 56 ofmetal (e.g., Cu) having a coefficient of thermal expansion higher thanthat of the metal layer 50 has been deposited thereon (e.g., bysputtering). Also, the sacrificial layer 46 has been removed (aspreviously described) from beneath the partially formed contact 16, asindicated by a dashed line, thereby freeing the contact 16 along most ofits length from the substrate 14. The metal layer 56 at its left end 58is joined onto an exposed portion of conductive circuit traces (notshown) and is thereby interconnected in a desired pattern with othercircuit elements (not shown), and also anchored onto the substrate 14. Ashort-length layer 60 of metal (e.g., Cr) having a coefficient ofthermal expansion like that of the metal layer 50 is selectivelydeposited (e.g., by sputtering) on top of the metal layer 56 near itsend 58. Before the insulating layer 54 is stripped away, and to form asmall contact area 62, particles of a hard abrasive contact material,such as micro-size conductive diamonds, are selectively deposited on thehard metal layer 52. The abbreviations Cu, Cr and W mean, respectively:copper, chromium, and tungsten.

Referring now to FIG. 10, there is shown the ultra-miniaturesurface-contacting electrical contact 16 after it has been fullyfabricated. The contact 16 was heated (e.g., above 300° C.) for a fewseconds which caused it to lift away for most of its length from thesubstrate 14 by the differential expansion of the metal layer 56 (highercoefficient of thermal expansion) relative to the metal layer 60 (lowercoefficient of thermal expansion). At the same time, by the differentialexpansion of the metal layer 56 (higher coefficient of thermalexpansion) and the metal layer 50 (lower coefficient of thermalexpansion), the contact 16 curled back beneath itself in a turn slightlymore than 360° to form a small diameter coil. After being so coiled themetal layers 50, 56 and 60 are over-plated by electrodeposition with alayer 64 of a specialized stiffening metal (Palladium M Series PlatingSolution) which substantially increases the strength and resiliency ofthe now completed contact 16. The contact 16 at its end 58 remainsanchored to the substrate 14, as was previously explained, and isinterconnected with other such contacts (see FIG. 1). By way of example,the length of the contact 16 can be about 150 microns, its width about40 microns, the thickness of the respective metal layers 50, 56, and 60,a few microns for each layer, the thickness of the stiffening metallayer 64 a few microns, and the coiled diameter of the contact 16 about50 microns. The curled-under configuration of the contact 16 improvesits performance and is an important design feature, as will now beexplained.

Referring to FIG. 11, a contact 16 (schematically shown) has its smallcontact area 62 (see also FIGS. 9 and 10) in initial contact with asurface pad 15 of a chip 12. By virtue of its curled-underconfiguration, that portion of the electrical contact 16 between itscontact area 62 and its stationary end 58 behaves like a cantileverbeam. Thus as the contact area 62 is pressed downward by the chip 12toward the substrate 14, the contact area 62 also moves to the right, asindicated by an arrow 72. This sidewise movement results in the surfaceof the pad 15 being “scraped” or rubbed free of oxide or insulating filmby the specially provided abrasive contact area 62.

Referring now to FIG. 12, the contact 16 is shown now fully engaging thesurface pad 15, and being compressed or squeezed between the substrate14 and the chip 12. The contact area 62 has now moved to the right sideof the pad 15 and a contacting portion of the electrical contact 16immediately to the left of the contact area 62 is pressed against thescraped-clean left side of the pad 15. Stable, low-resistance electricalconnection between the contact 16 and the pad 15 is accordinglyachieved. Depending on the relative lengths of the contact area 62 andthe pad 15, electrical connection may be entirely through the conductivediamonds of the area 62 to the pad 15, or partially through the diamondsand the metal layer 64, or solely through the metal layer 64 of thecontact 16. Because of the stiffening layer 64 of metal (see FIG. 10),the thus strengthened contact 16 is able to bear against the pad 15 withsufficient force and resiliency to insure such stable, low-resistanceconnection. When the chip 12 is thereafter disengaged from theelectrical contact 16, the latter will return substantially to itsinitial shape (see FIG. 10) without taking a “set”. This fact isimportant since it enables all of the contacts 16 in engagement witheach chip 12 to subsequently re-engage it or another like it, withforces above a minimum value required for stable connections. In actualmeasurements, a contact 16, having a stiffening metal layer 64, and witha 54-micron diameter coil was squeezed to a reduced height of about 25microns. The force required to do this was about 5 grams. The electricalcontact 16 when thereafter released, recovered to a 50-micron diameter.By contrast a 60-micron diameter contact like the contact 16 but withoutthe stiffening metal layer 64, had irreversible deformation or “set”when squeezed by more than 2 microns.

Referring now to FIG. 13, there is shown an enlarged schematic sideview, not to scale and partially broken away, of a partially fabricatedultra-miniature surface-contacting electrical contact 80 shown herestill in planar form, anchored at an end 82 to a substrate 84 (e.g.,silicon) on which is deposited a layer 86 of insulation (e.g., siliconnitride), a sacrificial layer 87 (e.g., SiO₂), a main layer 88 of metal(e.g., Cu) integral with the end 82, and a top layer 90 of metal 90(e.g., Cr) with a lower coefficient of expansion than that of the layer88. The steps in fabrication of the contact 80 are similar to onesdiscussed in connection with the contact 16 of FIG. 8.

Referring now to FIG. 14, there is shown a plan (top) view, partiallybroken away, of the contact 80 showing how the metal layers 88 and 90are patterned along their length from the fixed or left end 82 to aright end 92. The main layer 88 extends as a ribbon of uniform widthbeyond its end 82 to the end 92. On the other hand, the top metal layer90 extends over and along the layer 88 for a short distance from the end82, as indicated by a region 94, as a narrow strip 96 much narrower thanthe layer 88, and then broadens to the width of the layer 88 and extendsover it for the rest of its length to the end 92. Because the top metallayer 90 has a lower coefficient of thermal expansion than that of themain metal layer 88, when the sacrificial layer 87 is removed and thecontact 80 heated (in a way similar to that described in connection withFIGS. 8 and 9 and the contact 16) the contact 80 is raised along itslength above the substrate 84. Here, because the top metal layer 90 inthe region 94 is very narrow, the contact 80 is bent only slightly up inthis region, whereas for the rest of the length of the contact 80 beyondthe region 94 to its end 92, the contact 80 is curled back over itself.It is then as seen in FIG. 15 over-plated with a stiffening outer metallayer 98 (like the stiffening metal layer 64 shown in FIG. 9).

Referring now to FIG. 15, there is shown in schematic form a side viewof a fully fabricated contact 80 about to engage a surface pad 15 of achip 12. The contact 80, when the chip 12 and the substrate 84 arebrought closer together, will initially engage the pad 15 at a point“A”. Additional points “B” and “C”, which are also shown, are rotatedalong with the point “A” clockwise as the chip 12 and the substrate 84are moved closer and closer together. This rotation in turn, as shown inFIG. 16, results in a wiping or rubbing of the surface of the contact 80from point A to point B across the pad 15 (similar to the scrapingaction of the contact 16 illustrated in FIGS. 11 & 12). Point C, whichpreviously (FIG. 15) had been elevated as indicated at 99, is now downagainst the insulating layer 86 on the substrate 84. Thereafter thecontact 80 may be compressed (for a desired contact force) by furthermovement of the chip 12 toward the substrate 84 beyond the relativepositions shown in FIG. 16. If desired the contact 80 may be providedwith a special contact area (not shown) similar to the contact 62 of thecontact 16 in FIG. 11. By way of example, the contact 80 may have a coildiameter of about 60 microns, a width of about 40 microns, a flat lengthof about 150 microns, a length of the region 94 of about 40 microns, andthe thicknesses of the respective metal layers 88, 90, and 96 a fewmicrons each.

The above description is intended in illustration and not in limitationof the invention. Various changes in the contacts and in the methods offabrication described above may occur to those skilled in the art andmay be made without departing from the spirit of scope of the inventionas set forth in the accompanying claims. The invention is not limited tothe particular contact dimensions or materials mentioned, nor is itlimited to the specific sequence of process steps set forth. It is to benoted that some of the materials and process steps mentioned herein arealso described in the above-mentioned and incorporated by referencepatent application, Ser. No. 08/942,623, filed Oct. 2, 1997, even thoughthat patent application is directed to an invention different from thepresent invention described and claimed herein.

What is claimed is:
 1. An ultra-miniature electrical contact comprising:an elongated conductive body having two ends and formed of at leastthree layers of metals selectively deposited upon each other; the layerscomprising an inner layer, a middle layer, and an outer layer with themiddle layer being located between at least one portion of each of theinner and outer layers, the middle metal layer having a coefficient ofthermal expansion different from that of other layers; one end of thebody of the contact being adapted to be affixed to a substrate; theinner, middle, and outer layers being proportioned and disposed relativeto each other such that the body of the contact is bent by differentialexpansion of metal layers above the one end of the contact and thesubstrate; and at least a portion of the body of the contact near itsother end is bent down toward the substrate by differential expansion ofmetal layers.
 2. The contact of claim 1 wherein a stiffening outer metallayer is over-plated on the other layers from a palladium platingsolution to give substantial strength and resiliency to the contact. 3.The contact of claim 1 wherein the middle layer has a coefficient ofthermal expansion higher than that of the other layers.
 4. The contactof claim 1 wherein the middle layer has a coefficient of thermalexpansion lower than that of the other layers.
 5. The contact of claim 2wherein beyond its one end the body of the contact is curled underitself into a coil by differential expansion of the metal layers.
 6. Thecontact of claim 2 wherein the body of the contact closely adjacent itsother end is bent up by differential expansion of the metal layers. 7.The contact of claim 2 wherein the metal layers are roughly a fewmicrons thick, and the width of the layers is roughly 40 microns.
 8. Thecontact of claim 2 wherein the body of the contact has an abrasivecontact area at a location along its length.
 9. An ultra-miniatureelectrical contact comprising: an elongated conductive body formed of atleast two layers of different metals selectively deposited upon eachother; a portion of the contact being adapted to be fixed to asubstrate; a remaining portion of the contact being permanently bentinto a coil and lying above the substrate as a result of differentialexpansion of metal layers; and an outer stiffening metal layer beingdeposited over the plurality of metal layers, the stiffening metal layerbeing of metal electrodeposited from a palladium plating solution suchthat the contact has sufficient strength and resilience to effect stablelow-resistance connection to a member to be contacted.
 10. The contactof claim 9 wherein one metal layer is formed of copper, and anothermetal layer is formed of chromium.
 11. The contact of claim 9 whereinthe remaining portion of the contact is curled into a coil of at leastone turn and a few tens of microns in diameter, the coil being raisedabove the substrate such that the contact has a three-dimensional shapesuitable for contacting and wiping across a surface pad on an IC whenpressed between the pad and substrate.
 12. The contact of claim 11wherein the body of the contact has a special abrasive contact area at alocation along its length such that the contact area scrapes across thepad of an IC when pressed against it.
 13. An assembly of ultra-miniatureelectrical contacts mounted on a substrate and suitable for electricalcontact to contact areas of a device such as an integrated circuit, atleast one of the ultra-miniature electrical contacts comprising: anelongated conductive body having two ends and formed of at least twolayers of metals selectively deposited upon each other; one metal layerhaving a coefficient of thermal expansion higher than that of otherlayers; one end of the body of the contact being adapted to be affixedto the substrate, the body of the contact by differential expansion ofmetal layers being bent above the one fixed end of the contact and thesubstrate; at least a portion of the body of the contact near its otherend being bent down toward the substrate as a result of differentialexpansion of metal layers; and an outer stiffening metal layer beingelectrodeposited on the other layers to give substantial strength andresiliency to the contact.
 14. The contact of claim 13 wherein beyondits fixed one end the body of the contact is curled under itself in acoil.
 15. The contact of claim 13 wherein the body of the contact alongits length and toward its other end is bent both up and down bydifferential expansion of the metal layers into a free-standing shapesuitable for connecting to contact areas along the edge of a circuitcard.
 16. The contact of claim 14 wherein the body of the contact has ahard abrasive contact area at a location along its length.
 17. Anassembly of ultra-miniature electrical contacts mounted on a substrateand suitable for making electrical contact to surface pads of a devicesuch as an integrated circuit (IC), said assembly comprising: asubstrate; an elongated conductive body formed on the substrate as atleast two layers of different metals selectively deposited upon eachother, one layer being a thin ribbon-like strip continuous along thebody, another layer being selectively deposited on the one layer for ashort distance along the one layer; a portion of the contact beingaffixed to the substrate; a remaining portion of the contact beingpermanently bent into a three-dimensional shape above the substrate as aresult of differential expansion of metal layers; and an outerstiffening metal layer being deposited over the plurality of metallayers such that the contact has sufficient strength and resilience toeffect stable low-resistance electrical contact to a surface pad of anIC device.
 18. The contact of claim 12 wherein one metal layer is formedof copper, and another metal layer of chromium, the outer stiffeningmetal layer being of metal electrodeposited from a palladium platingsolution.
 19. The contact of claim 17 wherein the three-dimensionalportion of the contact is curled back under itself into a coil of morethan one turn and has a hard abrasive contact area at a given locationsuch that the hard contact area scrapes across the pad of an IC whenpressed against it.
 20. The contact of claim 17 wherein thethree-dimensional portion of the contact is slightly bent above thesubstrate for a short length beyond the fixed portion and is thereaftercurled back over itself into a coil of more than one turn such thata'surface of the contact wipes across the pad of an IC when pressedagainst it.
 21. The contact of claim 20 wherein a first metal layer hasa first coefficient of thermal expansion and a ribbon-like width alongits length, and a second metal layer has a second coefficient of thermalexpansion lower than the first, the second layer in the short lengthbeyond the fixed portion having a width less than the width of the firstlayer, and thereafter having a width substantially equal to the width ofthe first layer.